HBM 5510
HBM 5510 is a high density polyethylene, specially developed for large parts blow molding
Description
HBM 5510
High Density Polyethylene
Product Description
HBM 5510 is a high density polyethylene, specially developed for large parts blow molding. This grade, which is produced by 1-hexene as a co-monomer, offers high stiffness, good process-ability, excellent parison melt strength and good ESCR. HBM 5510 has been manufactured under Basell license.
General Information
| Status | Commercial: Active | |
| Application | Large Parts Blow Molding – Standard and Lightweight Jerry Cans- Open Top Drums (Up to 110 lit). | |
| Form(s) | Pellet | |
| Attribute | Good ESCR
Good Stiffness |
Good Process-ability |
| Additives | Antioxidant: Yes
Processing Aid: No |
Antiblock: No
Slip Agent: No |
| Typical Properties | Typical Value 1 | Unit | Test Method |
| Physical | |||
| High Load Melt Flow Index (190oC/ 21.6 kg) | 10 | g/10 min | ISO 1133 |
| Melt Flow Index (190oC/ 5 kg) | 0.50 | g/10 min | ISO 1133 |
| Density 2 | 0.955 | g/cm3 | ISO 1183 |
| Bulk Density | > 0.50 | g/cm3 | ISO 60 |
| Mechanical 3 | |||
| Tensile Modulus of Elasticity | 1000 | MPa | ISO 527-1,2 |
| Flexural Modulus – 1% Secant | 1000 | MPa | ASTM D790 |
| Tensile Stress at Yield | 27 | MPa | ISO 527-1,2 |
| Tensile Strain at Yield | 8 | % | ISO 527-1,2 |
| Tensile Stress at Break | 43 | MPa | ISO 527-1,2 |
| Ball Indentation Hardness | 49 | MPa | ISO 2039-1 |
| ESCR F50 (100% Igepal, Method B) | 110 | hrs | ASTM D1693 |
Impact
| Tensile Impact Strength (Notched, Type 1, Method A, -30oC) | 135 | kJ/m2 | ISO 8256 |
| Izod Impact Strength (Notched, Method A, 23oC) | 22 | kJ/m2 | ISO 180 |
| Thermal | |||
| Vicat Softening Temperature (Method A/ 10N) | 127 | oC | ISO 306 |
| Deflection Temperature Under Load (1.8 MPa) | 45 | oC | ISO 75 |
| Recommended Process Conditions 4 | |||
| Extruder Barrel Temperature: 180-220 °C | Melt Temperature: 200-235 °C | ||
- Typical values: these are not to be construed as
- The density parameter was determined on compression-molded specimens, which were prepared in accordance with procedure C of ASTM D4703, Annex A1.
- Properties are based on compression-molded specimens, which were prepared in accordance with procedure B of ASTM D4703, Annex A1, using 100% HBM 5510 resin.
- Please note that, these processing conditions are recommended by manufacturer only for 100% HBM 5510 resin (not in the case of blending with any other compatible material), therefore because of the many particular factors which are outside our current knowledge and control and may affect the use of product, no warranty is given for the foregoing Moreover, the specific recommendations for resin type and processing conditions can only be made when the end use, required properties and fabrication equipment are known.
Additional information
| MFI (dg/min): | 10 (190oC/ 21.6 kg) |
|---|---|
| Density (kg/m3): | 955 |
| Application(s): | Large Parts Blow Molding – Standard and Lightweight Jerry Cans- Open Top Drums |