BL3
HF-4760 (BL3) is a blow molding grade resin with high density polyethylene with 1-Butene as co monomer which is manufactured by the suspension polymerization of ethylene monomer.
Description
BL3
High Density Polyethylene, Blow molding
Applications:
- Small blow moulding,
- Bottles
- Containers (up to 5 lit)
- Packaging of pharmaceuticals & surfactants
| Resin Properties | Unit | Value | Test Method |
| Mass density (23℃) | g/cm3 | 0.945 | ISO 1183 |
| Melt Flow Rate ( 190℃/ 5.06kg) | (g/10 min) | 1.2 | ISO 1133 |
| Melt Flow Rate ( 190℃/ 21.16kg) | (g/10 min) | 23 | ISO 1133 |
| FRR | – | 19 | |
| Impact Strength (23℃) | Mj/mm2 | 10 | ISO 179/1eA |
| Swell ratio | % | 120 | MPC-test |
| Flexural Creep Modulus (4 Point, 1 min) | Mpa | 1300 | DIN 19537-2 |
| Tensile Modulus (23℃, v=1mm/min, secant) | Mpa | 1250 | ISO 527 |
| Strength at Break | Mpa | 32 | ISO 527 |
| Elongation at Break | % | >600 | ISO 527 |
| Elongation at Yield | % | 10 | ISO 527 |
| Softening Temperature | C | 77 | ISO 306 |
| BrittleTemperature | C | <-80 | ASTM D746-72 |
| Shore D hardness | 62 | ISO 868 | |
| ESCR in full notch creep test (80℃, 2%Arcopal) | h@3.5 MPa | 5 | ISO CD 16770 |
Additional information
| MFI (dg/min): | 1.2 (190°C /5 kg) |
|---|---|
| Density (kg/m3): | 945 |
| Application(s): | Small blow moulding, Bottles, Containers (up to 5 lit), Packaging of pharmaceuticals & surfactants |